Susceptibility of welded X80 pipeline steel to corrosion in simulated soil solution

You are here: Homepage > Search

Susceptibility of welded X80 pipeline steel to corrosion in simulated soil solution

Susceptibility of welded X80 pipeline steel to corrosion in simulated soil solution

Ren, C.Q. / Xian, N. / Wang, X. / Liu, L. / Zheng, Y.P.

This work is focused on the corrosion behaviour of weldments in X80 pipeline steel. In order to clarify their susceptibility to soil corrosion, general corrosion and stress corrosion crack experiments were carried out in a simulated soil solution (g/L: 0.483 NaHCO3, 0.131 MgSO4.7H2O, 0.127 CaCl2, 0.122 KCl). Based on these results, the heat affected zone (HAZ) demonstrated higher corrosion susceptibility than the base metal and the weld metal. This was due to both the higher intrinsic corrosion rate of the HAZ and the galvanic effects between the HAZ and the other regions of the weldment. Additionally, in slow strain rate testing, corrosion damage in the HAZ resulted in a significant decrease in fracture area reduction and time to failure and an increase in the appearance of brittle failure on the fracture surface compared with the base metal. Elemental segregation and coarse grains appear to be two factors that lead to the high corrosion of HAZ.

Access

Check availability in my library

Order at Subito €

Export, share and cite

Document information

Title :

Susceptibility of welded X80 pipeline steel to corrosion in simulated soil solution

Additional title:

Korrosionsempfindlichkeit von geschweißtem Rohrstahl X80 in simuliertem Erdboden

Contributors:

Ren, C.Q. (author) / Xian, N. (author) / Wang, X. (author) / Liu, L. (author) / Zheng, Y.P. (author)

Published in:

Corrosion Engineering, Science and Technology ; 47 , 6 ; 441-445

Publication date :

2012

Size :

5 Seiten, 9 Bilder, 4 Tabellen, 22 Quellen

ISSN :

DOI :

https://doi.org/10.1179/1743278212Y.0000000025

Type of media :

Article (Journal)

Type of material :

Print

Language :

English

Keywords :

Spannungsrisskorrosion , Rohrstahl , Empfindlichkeitsanalyse , Erdboden , Schweißverbindung , Simulationsversuch , Wärmeeinflusszone , Korrosionsmechanismus , Korrosionsgeschwindigkeit , Mikrohärte , Spannungs-Dehnungs-Verhalten , Polarisationskurve

Similar titles

Study of AC corrosion on coated pipeline steel in simulated soil solution

Xu, Xin / Xu, Lining / Liu, Wei et al. | Tema Archive | 2011

STEEL TUBING, CORROSION RESISTANT WELDED

SAE Technical Papers | 1944

Grooving corrosion of a 24-in seam welded pipeline

El-Sayed, Mohamed Hanafy | Tema Archive | 2014

Transgranular stress corrosion cracking of X-60 pipeline steel in simulated ground water

Zhang, X.Y. / Lambert, S.B. / Sutherby, R. et al. | Tema Archive | 1999

Steel, Corrosion Resistant, Welded Tubing 19Cr - 9.5Ni (304) Solution Heat Treated

SAE Technical Papers | 2013

Access

Check availability in my library

Order at Subito €

Page navigation

Document information

Export, share and cite