Warm-mix asphalt (WMA) technology is developed by lowering the binder melting point, which may cause WMA to be weak against rutting at high service temperatures. Much research has been done on the high-temperature characteristics of WMA mixtures, but the low-temperature fracture behavior that leads to cracking has not been well evaluated. Because WMA is produced at lower temperatures with a lower aggregate heating, the behavior at the interface where the binder is coating aggregate is in question at low temperatures. In this study, 13-mm, dense-grade WMA mixtures were produced by using WMA binders. Beam specimens were prepared for fracture toughness (KIC) evaluation at −20°C by a three-point bending test. The results and analyses revealed that the KIC values of WMA mixtures at −20°C were similar to or better than those of HMA mixtures, even though they were produced at temperatures 30°C or 40°C lower than HMA mixtures.


    Zugriff

    Download

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Low-Temperature Fracture Characteristics of Selected Warm-Mix Asphalt Concretes


    Weitere Titelangaben:

    Transportation Research Record


    Beteiligte:
    Yoo, Min-Yong (Autor:in) / Jeong, Seung-Ho (Autor:in) / Park, Ji-Yong (Autor:in) / Kim, Nam-Ho (Autor:in) / Kim, Kwang-Woo (Autor:in)


    Erscheinungsdatum :

    2011-01-01




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch





    Evaluation of Fracture Toughness of Semirigid Asphalt Concretes at Low Temperatures

    Baek, Sung-Hyun / Hong, Jun-Pyo / Kim, Sung Un et al. | Transportation Research Record | 2011


    Evaluation of selected warm mix asphalt technologies

    Sebaaly, Peter E. / Hajj, Elie Y. / Piratheepan, Murugaiyah | British Library Online Contents | 2015


    Low Temperature Behavior of Asphaltite Modified Binders and Asphalt Concretes

    Themeli, Andrea / Chailleux, Emmanuel / Chazallon, Cyrille et al. | TIBKAT | 2020