Since early 1860's rail vehicle axles are examined with regard to their structural durability. August Woehler was the first engineer who was working on this topic by means of cyclic loading which was evaluated to be a root cause for early in-service termination by fatigue phenomena. Different to static loads the effect of cyclic loading is time dependent: By every load cycle an incremental damage is created which may evolve to fatigue failure. Hence the huge number of load cycles within the life cycle of rail vehicles, which may for axles, will create operational incidents, or - even worse - fatigue cracks. Since it is proven that there is no endurance limit for engineered parts, the design validation process has to be reviewed for components which were created assuming an endurance limit and infinite life. The DT2.5/DT3 wheel set axles of Hamburger Hochbahn metro vehicles are such components which are currently running at >2.5 mio. km and will be used beyond 2012 having an annual mileage of more than 100,000 km. For one of those axles a fatigue crack at the area of the wheel press fit was monitored by regular ultrasonic inspection technology. Due to the unknown crack propagation rate for in-service loading the safety check by ultrasonic examination was reduced to an interval of 39,000 km, which created a major impact on costs and availability of these vehicles. Therefor the Hamburger Hochbahn AG organisation worked together with Fraunhofer LBF on a fail-safe concept which was developed on experimental crack growth data created by laboratory service load simulation of the DT2.5/DT3 axles.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Development of a fail-safe concept for metro vehicle axles by using crack growth results from service load simulation


    Beteiligte:
    Liedgens, K. (Autor:in) / Heim, R. (Autor:in)


    Erscheinungsdatum :

    2009


    Format / Umfang :

    11 Seiten, 10 Bilder, 1 Tabelle, 4 Quellen



    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Development of a Sealing Concept for Off-Road Vehicle Axles

    Vogt,R. / Freudenberg Simrit,C. / Seidl,J. | Kraftfahrwesen | 1993


    Simulation of fatigue crack propagation in railway axles

    Beretta, S. / Carboni, M. | Tema Archiv | 2005


    Development of a sealing concept for off-road vehicle axles

    Vogt, R. / Freudenberg Simrit, C. / Seidl, J. | Tema Archiv | 1993


    Investigations of fatigue crack growth in wheelset axles

    Sander, M. / Richard, H.A. | Tema Archiv | 2009


    Development of a Sealing Concept for Off-Road Vehicle Axles

    Simrit, Carl Freudenberg / Seidl, Josef / Vogt, Rolf | SAE Technical Papers | 1993