As the deep submersible vehicle is subject to severe conditions in deep sea, it is essential that the materials used for pressure hull should have performance with regards to fracture toughness, fatigue properties, stress corrosion cracking properties and so on. Especially, the properties to resist the stress corrosion cracking is the most significant problem of the materials for pressure hull. From this view point, the authors have investigated the stress corrosion cracking of 10Ni-8 Co steel and its weld joint for several years and made clear the effect of heat treatment conditions, shielding conditions in GTA welding and fabricational conditions. The conclusions are that 10Ni-8Co steel is usable as a material for the construction of the pressure hull of the deep submersible vehicle from viewpoint of stress corrosion cracking.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Stress corrosion cracking of high strength steel for pressure hull of deep submersible vehicle


    Weitere Titelangaben:

    Spannungsrisskorrosion bei hochfestem Stahl fuer den Druckbehaelter eines Tiefsee-U-Bootes
    Titel japanisch


    Beteiligte:
    Yamada, S. (Autor:in) / Matsumura, H. (Autor:in) / Ikeda, T. (Autor:in) / Takasugi, N. (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    1981


    Format / Umfang :

    9 Seiten, 16 Bilder, 3 Tabellen, 6 Quellen


    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Japanisch




    SUBMERSIBLE VEHICLE HULL

    YAMASHITA SHOZO | Europäisches Patentamt | 2020

    Freier Zugriff


    SUBMERSIBLE MULTI-HULL CRAFT

    ALLEN GRAHAM LOCKHART | Europäisches Patentamt | 2019

    Freier Zugriff


    Strength effect in stress corrosion cracking of high-strength steel in aqueous solution

    Li, H.L. / Gao, K.W. / Qiao, L.J. et al. | Tema Archiv | 2001