Generally brake pads are manufacturing by use of asbestos materials, that materials are chemically harmful and toxic nature to affect the human health. The present investigation is to fabricates polypropylene composites with mixing constant volume [5 vol.%] of alumina nano particles and different volume percentages [0%, 5%, 10% & 15%] of basalt Fiber by hand layup compression technique. The wear characteristics of polypropylene matrix composites were tested by dry sliding condition. The test was carried out pin on disc apparatus, configured with hardened steel counter-face at elevated temperature. The load was applied 10 N to 30 N with the interval of 10 N and varying of sliding speed 300 rpm to 900 rpm with the interval of 300 rpm for the time period of 0-180 sec. The wear rate was decreases with addition of alumina nano particle and the frictional force was increases due to basalt Fiber content present in the composites. The co-efficient of friction was increases 0.1 to 0.66 under normal loading condition.
Fabrication and Wear Characteristics Basalt Fiber Reinforced Polypropylene Matrix Composites
Sae Technical Papers
NuGen Summit ; 2019
2019-11-21
Aufsatz (Konferenz)
Englisch
Particulate matter (PM) , Hand , Composite materials , Steel , Fabrication , Fibers , Brake pads , Wear
Thermal characteristics of basalt fiber reinforced epoxy-benzoxazine composites
British Library Online Contents | 2012
|Experimental Research on Basalt Fiber Reinforced Cementitious Composites
British Library Conference Proceedings | 2013
|Wear properties of glass fiber reinforced polypropylene
Kraftfahrwesen | 2012
|Optimal Design for Hybrid Ratio of Carbon/Basalt Hybrid Fiber Reinforced Resin Matrix Composites
DOAJ | 2017
|