The results of constant amplitude fatigue loading of FRP laminates fabricated with resins of various styrene levels are discussed. Laminates were prepared using a commercially available polyester resin with 40 %, 35 % and 30 % monomer content (styrene). Flexural stiffness retention vs. number of fatigue cycles were compared. The rate and percentage of stiffness reduction were comparable between the laminates constructed with the 40 % and 35 % level styrene resins, while all samples made from the 30 % styrene content resin failed pre-maturely. All samples were initially stressed at 35 % of ultimate flexural strength, and all samples indicated matrix failure of the composite.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Fatigue testing of low styrene content resin composite laminates


    Weitere Titelangaben:

    Ermüdungstest von Verbundschichtwerkstoffen aus Harz mit geringem Styren-Anteil


    Beteiligte:
    Rohan, N. (Autor:in)


    Erscheinungsdatum :

    1992


    Format / Umfang :

    11 Seiten, 4 Bilder, 2 Tabellen, 6 Quellen


    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Determining resin/fiber content of laminates

    Garrard, G. G. / Houston, D. W. | NTRS | 1979


    Creep/Fatigue Behavior of Resin Infused Biaxial Glass Fabric Laminates

    Mandell, John F. / Miller, David / Samborsky, Daniel | AIAA | 2013


    Creep/Fatigue Behavior of Resin Infused Biaxial Glass Fabric Laminates

    Mandell, J.F. / Miller, D. / Samborsky, D. et al. | British Library Conference Proceedings | 2013


    Fatigue life methodology for tapered composite flexbeam laminates

    Murri, G.B. / O'Brien, T.K. / Rousseau, C.Q. | Tema Archiv | 1998