The high temperature dry sliding wear behaviour of Ti-6Al-4V alloy was analyzed using a pin-on-disk wear testing equipment with commercial brake pad as a counterface material, The experiment was carried out at loads of 1 kg and 2 kg and at velocities of 1 m/s and 2 m/s. The temperature was varied at 27 °C, 200 °C and 300 °C with a constant sliding distance of 2000 m. The mass loss of both disc and pin was measured and correlated with the test parameters. The load found to have significant influence on mass loss compared to velocity. The SEM images of worn out samples revealed ploughing, chip and debris formations during sliding against brake pad.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Wear analysis of Ti-6Al-4V alloy - brake pad pair for automobile/aircraft disc brakes at elevated temperatures


    Beteiligte:
    Duraiselvam, M. (Autor:in) / Naveen, R. (Autor:in) / Natarajan, S. (Autor:in) / Satish, M. (Autor:in)


    Erscheinungsdatum :

    2010


    Format / Umfang :

    5 Seiten, 3 Bilder, 11 Quellen



    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Electromechanical brake actuator for disc brakes

    BEIER PETER / HENNING PAUL / TOMALA BARTLOMIEJ | Europäisches Patentamt | 2023

    Freier Zugriff

    Pad Wear Indication for Disc Brakes

    Hattwig, Peter | SAE Technical Papers | 1975


    Pad wear indication for disc brakes.

    Hattwig,P. / Volkswagen | Kraftfahrwesen | 1975


    Pad wear indication for disc brakes

    Hattwig, P. | Tema Archiv | 1975


    Automobile automatic alarm brake system with dual brakes

    HU QINGGUI | Europäisches Patentamt | 2015

    Freier Zugriff