Compositions in the mixed strontium/calcium feldspar ([Sr/Ca]O·Al2O3·2SiO2) - aluminum titanate (Al2O3·TiO2) system have been investigated as alternative materials for the diesel particulate filter (DPF) application. A key attribute of these compositions is their low coefficient of thermal expansion (CTE). Samples have been prepared with porosities of >50% having average pore sizes of between 12 and 16μm. The superior thermal shock resistance, increased resistance to ash attack, and high volumetric heat capacity of these materials, coupled with monolithic fabrication, provide certain advantages over currently available silicon carbide products. In addition, based on testing done so far aluminum titanate-based filters have demonstrated chemical durability and comparable pressure drop (both bare and catalyzed) to current, commercially available, silicon carbide products.
Aluminum Titanate Compositions for Diesel Particulate Filters
Sae Technical Papers
SAE 2005 World Congress & Exhibition ; 2005
2005-04-11
Aufsatz (Konferenz)
Englisch
2005-01-0583 Aluminum Titanate Compositions for Diesel Particulate Filters
British Library Conference Proceedings | 2005
|Aluminium titanate compositions for diesel particulate filters
Kraftfahrwesen | 2005
|Performance Evaluations of Aluminum Titanate Diesel Particulate Filters
SAE Technical Papers | 2007
|Performance Evaluations of Aluminum Titanate Diesel Particulate Filters
British Library Conference Proceedings | 2007
|Performance evaluations of aluminium titanate diesel particulate filters
Kraftfahrwesen | 2007
|