Seven boron/epoxy double-wall shafts were ballistically impacted while under torque loads ranging from 7,500 to 12,300 i.-lb. Projectile velocities ranged from 1,540 to 2,500 fps. Static residual strength tests were then conducted. Three aluminum shafts were tested similarly for comparison. The residual strength of the boron/epoxy shafts was approximately 8,000 in.-lb, which is about one-third the ultimate strength of an undamaged tube. The aluminum shafts exhibited residual strengths of 22,000 to 32,000 in.-lb, which would be sufficient to carry expected flight loads. (Author)


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Ballistic Vulnerability of Boron/Epoxy Double-Wall Drive Shafts


    Beteiligte:
    R. T. Welge (Autor:in) / F. H. Veit (Autor:in)

    Erscheinungsdatum :

    1971


    Format / Umfang :

    45 pages


    Medientyp :

    Report


    Format :

    Keine Angabe


    Sprache :

    Englisch




    DRIVE SHAFTS

    SALTER BENJAMIN GUY | Europäisches Patentamt | 2015

    Freier Zugriff

    DRIVE SHAFTS

    SALTER BENJAMIN GUY | Europäisches Patentamt | 2015

    Freier Zugriff

    DRIVE SHAFTS

    SALTER BENJAMIN GUY | Europäisches Patentamt | 2016

    Freier Zugriff

    Concentric drive shafts

    SALTER BENJAMIN | Europäisches Patentamt | 2015

    Freier Zugriff

    Heat treating automobile drive shafts

    Engineering Index Backfile | 1920